We are the authorized distributor of PVC Resin for M/s. DCW Ltd. in western region of India. DCW Ltd is the pioneer of PVC Resins manufacturing technology in India since 1970. Petrochemicals has been the new buzzword of Indian industry in recent years. In 1970, DCW became one of the first in India to enter this growing field by setting up a PVC resin plant at Sahupuram in Tamil Nadu in Southern India.
DCW was the first, and is currently the only Indian producer to handle and store imported VCM, a volatile gas. It successfully erected a total storage capacity of 5,600 MT at Tuticorin port (a distance of 30 km from the plant) - including a huge 5000 M3 sphere. This installation is one of the few of its kind in South East Asia and gives the company a competitive edge in meeting its import requirements.
| Typical Properties | Unit | Method of Analysis | |
| K-Value | ISO/R-174-1961 | 64-66 | |
| Bulk Density | gms/cc | IS 4669 –1968 | 0.50 +/- 0.01 |
| Volatile Matter Max | % | IS 4669 – 1968 | 0.30 |
| Seive Analysis 42 Mesh | % | IS 460 – 1962 | 99.90 |
| Foreign Matter / 100 gms | nos. | As per Japanese Std | 32 |
| Residual VCM ppm | ppm | ASTM D/3749 – 1987 | 2 ppm max |
| Thermal Stability | min | IS 4669 – 1968 | 2 – 3 Min |
| Plastisizer Aborption | phr | IS 4669 – 1968 | 38 – 41 phr |
| Sr. No. | Test | Unit | Method | Result |
| 1 | Specific Gravity | - | ASTM D 792 | 1.49 |
| 2 | Vicat Softening Temp at 5 kg load | deg.C | ASTM D 1525 | 102.0 |
| 3 | Heat Deflection Temp at 264 Psi (Annealing at 100°C for 24 hours) | deg.C | ASTM D 648 | 100 |
| 4 | Tensile Strengh at yeild | Mpa | ASTM D 638 | 55 |
| 5 | Tensile Modulus | Mpa | ASTM D 638 | 2531 |
| 6 | Flexural Strengh at yeild | Mpa | ASTM D 790 | 114 |
| 7 | Flexural Modulus | Mpa | ASTM D 790 | 3833 |
| 8 | Notched Izod Impact Strengh | J/m | ASTM D 256 | 126 |
| Sr. No. | Test | Unit | Method | Result |
| 1 | Chlorine Content | Wt % | - | 67.1 |
| 2 | Bulk Density | Gm/cm3 | ISO 60 | 0.6761 |
| 3 | Foreign Particles | Nos/100gm | ISO 1265 | 14.0 |
| 4 | K-Value of PVC Resin | - | ISO 1628-2 | 57.6 |
| Sr. No. | Test | Unit | Method | Result |
| 1 | Chlorine Content | Wt % | - | 67.4 |
| 2 | Bulk Density | Gm/cm3 | ISO 60 | 0.6409 |
| 3 | Foreign Particles | Nos/100gms | ISO 1265 | 13.0 |
| 4 | K-Value of PVC Resin | - | ISO 1628-2 | 66.0 |